Epoxidation process with improved heterogeneous catalyst

ABSTRACT

Solid chemical combinations of certain metal oxides or hydroxides with oxygen compounds of silicon give improved performance as catalysts for the epoxidation of olefinically unsaturated compounds with organic hydroperoxides when the catalysts are first treated with an organic silylating agent at an elevated temperature.

United States Patent Wulff Dec. 2, 1975 EPOXIDATION PROCESS WITH IMPROVED [56] References Cited lnvenwrr Harald Wulff, Alameda, Calif- 3,332,965 7/1967 Fukui et a] 260/3485 R [73] Assignee: Shell Oil Company, Houston, Tex.

Primary ExaminerNorma S. Milestone [22] Filed: Dec. 7, 1973 [21] Appl. No.: 422,950 [57 ABSTRACT Related Application Data Solid chemical combinations of certain metal oxides [60] Division of Ser. No. 234,301, March 13, 1972, Fat. or hydroxides with oxygen compounds of silicon give No. 3,829,392, which is a continuation-in-part of Ser. improved performance as catalysts for the epoxidation 1, 1970- abandonedof olefinically unsaturated compounds with organic hydroperoxides when the catalysts are first treated U-S. Cl-

L an rganic agent at an elevated temper. [5 1] Int. Cl. C07D 301/20 ature [58] Field of Search 260/3485 L 18 Claims, N0 Drawings EPOXIDATION PROCESS WITH IMPROVED IIETEROGENEOUS CATALYST CROSS REFERENCES TO RELATED i APPLICATIONS This is a division of application Ser. No. 234,301 filed Mar. 13, 1972 now US. Pat. No. 3,829,392 which is a continuation-in-part of application Ser. No. 77,385 filed Oct. 1, 1970 now abandoned.

The subject matter of this application is related to the following US. patent applications: Ser. Nos. 812,920, 812,923 and 812,924, all filed Apr. 2, 1969, by H. P. Wulff and F. Wattimena and now abandoned; copending Ser. Nos. 173,325 and 173,326 filed Aug. 19, 1971, as continuations-in-part of said Ser. No. 812,920; Ser. No. 868,584 filed Oct. 22, 1969, by F. Wattimena and now abandoned; and Ser. No. 812,922 filed Apr. 2, 1969, by H. P. Wulff and F. Wattimena, now US. Pat. No. 3,634,464. The disclosures of said US. Pat. No. 3,634,464 and of said related applications Ser. Nos. 812,920, 812,923, 812,924 and 868,584 are incorporated herein by reference and copies of the specifications of said four applications have been placed in the file of the present application.

BACKGROUND OF THE INVENTION Wattimena and Ser. No. 868,584, filed Oct. 22, 1969 by Wattimena, it is shown that certain metal oxides and hydroxides, for example, the oxides and hydroxides of titanium, molybdenum, vanadium, zirconium and boron, when chemically combined with inorganic siliceous oxides, for example silica, are effective heterogeneous catalysts for the reaction of olefins with organic hydroperoxides to form olefin oxides. In such an olefin epoxidation reaction, an olefin is mixed with an organic hydroperoxide and passed over the metal oxide siliceous oxide catalyst. Ideally, the catalyst should cause the hydroperoxide to react exclusively with olefin to produce only olefin oxide. In other words, the catalysts should be 100% selective to the olefin epoxidation reaction. In fact, as with virtually all heterogeneously catalyzed reactions, only a substantial proportion, and not all of the hydroperoxide which reacts, reacts with olefin to form olefin epoxide in the presence of these known catalysts. The remainder of the reacting hydroperoxide forms less desirable by-products. Because of the wellknown high reactivity of hydroperoxides and the general tendency of peroxides to decompose to nondesired products in the presence of a great number of catalyst materials, the search for ways to improve the selectivity of heterogeneous catalysts for epoxidation of olefins with organic hydroperoxides is especially important and also especially difficult.

STATEMENT OF THE INVENTION It has now been found that epoxidation catalysts comprising an inorganic oxygen compound of silicon in chemical combination with certain metal oxides or hydroxides are improved and catalyze the epoxidation reaction of olefinically unsaturated hydrocarbons with organic hydroperoxides to give olefin oxides with improved efficiency when these catalysts are treated prior to use by contact with an organic silylating agent at elevated temperatures.

More especially, it has been found that processes for preparing olefin oxides by reacting olefins with organic hydroperoxides in the presence of metal oxide-siliceous solid heterogeneous catalysts at temperatures of from 25C to 200C are improved when the catalysts are contacted with an organic silylating agent at temperatures of up to about 450C prior to use. In a particularly preferred embodiment of the invention, contacting metal oxide silica materials (such as titania-silica) with an organic silylating agent (such as an organic halosilane or an organic silazane) at temperatures of from C to 450C makes the resulting materials better, more efficient, and more selective catalysts for the epoxidation of olefins with organic hydroperoxides.

DETAILED DESCRIPTION OF THE INVENTION The Catalysts Treated. The catalysts which are improved by silylation in accordance with the invention are olefin epoxidation catalysts consisting essentially of a solid inorganic oxygen compound of silicon in chemical combination with at least about 0.1% by weight of an oxide or hydroxide of titanium, molybdenum, vanadium, zirconium or boron. These metal oxide-hydroxide/siliceous oxide composites and methods for their preparation are described in the above listed U.S. applications Ser. Nos. 812,920, 812,922, 812,923, 812,924 and US. Pat. No. 3,634,464. The oxygen compound of silicon employed is a siliceous solid containing a major proportion of silica. In general, suitable inorganic siliceous solids are further characterized by having a relatively large surface area in relation to their mass. The term used herein and one normally used in the art to express the relationship of surface area to mass is specific surface area. Numerically, specific surface area will be expressed as square meters per gram (m /g). Generally the inorganic siliceous solid has a specific surface area of at least 1 m /g and preferably the average specific surface area is from 25 m /g to 800 m /g.

One class of suitable inorganic siliceous solid is synthetic, porous silica consisting of particles of amorphous silica flocculated or linked together so that they form relatively dense, close-packed masses. Representatives of such materials are silica gel and precipitated silica. These silica products are porous, in that they have numerous pores, voids or interstices throughout their structures. The preparation and properties of such porous siliceous solids are described by RC. Iler, The Colloid Chemistry of Silica and Silicates, Cornell University Press, New York, 1955, Chap. VI and US. Pat. No. 2,657,149 of R. G. Iler, issued Oct. 27, 1953. A variety of silica gels are available commercially. Commercial silica gels consisting of at least 99% silica and having specific surface area of about 25 m /g to about 800 Another class of suitable inorganic siliceous solids are synthetic silica powders consisting of particles of amorphous silica flocculated in open-packed, readily disintegrated, loosely-knit aggregates. Representatives of silica powders are fumed, pyrogenic silicas obtained by the combustion of hydrogen and oxygen with silicon tetrachloride or tetrafluoride. Fumed silicas are produced commercially and are sold by various companies such as by Cabot Corporation as Cab-O-Sil" and by Degussa as *Aerosil". Fumed silicas suitably employed as catalyst generally consist of at least 99% silica and have surface area of about 50 m /g to about 400 m /g and particle size of about 0.007 micron to about 0.05 micron.

Other classes of inorganic siliceous solids are synthetic inorganic oxide materials containing a major portion of silica, known as refractory oxides. and naturally-occurring crystalline mineral silicates.

Synthetic amorphous inorganic siliceous solids are preferred over naturally-occurring crystalline mineral silicates as catalyst precursors. Particularly preferred synthetic inorganic siliceous solids are those consisting essentially of pure silica, e.g., at least 90% silica.

Chemically combined with the siliceous solid, in catalysts improved by the process of the invention, is a metal oxide or hyroxide. Suitable metal oxides or hydroxides include those of titanium. vanadium, boron, molybdenum and zirconium.

Generally, the catalysts contain from about 0.2 to by weight (basis catalyst) of such metal oxides or hydroxides. Very suitable catalysts contain from 0.5 to 8% by weight of an oxide or hydroxide of titanium in chemical combination with silica.

A most preferred catalyst for treatment by this invention consists essentially of silica chemically combined with from 0.5 to 5% by weight of titanium oxide.

The oxide or hydroxide of titanium is preferably combined with the oxygen compound of silicon in a high positive oxidation state, e.g., tetravalent titanium. The proportion of the oxide or hyroxide of titanium combined in the catalyst composition can be varied, but generally the catalyst composition contains at least 0.1% by weight of the oxide or hyroxide of titanium with amounts from about 0.2% to about 50% by weight being preferred, although still larger (major) proportions of titanium oxide or hydroxide can be used.

The catalyst compositions which are to be treated suitably incorporate non-interfering and/or catalyst promoting substances, especially those which are chemically inert to the reactants and products. The catalysts may incorporate minor amounts of promoters, for example, the'alkali metals or alkaline earth metals, as oxides or hyroxides. Alkali metal additions of from 0.01 to about 5% by weight (basis catalyst) are preferred as promoters. 7

An excellent catalyst for treating in accordance with this invention consists essentially of silica chemically combined with from 0.5 to 5% by weightof titanium oxide and from 0.01 to 5% by weight of calcium (as the oxide) as promoter.

The catalyst compositions are prepared by a variety of methods, including impregnation of a siliceous support with a suitable metal-containing solution followed by heating, cogelling the metal hydroxide and silica,

and by calcining together a mixture of inorganic sili-.

ceous solid and metal oxides at elevated temperatures.

In still another technique, the catalyst composition is 7 prepared by the surface reaction of silanol groups of an inorganic siliceous solid with a titanium salt by the procedure disclosed in 1.1.5. Pat. No. 3,166,542 of Orzechowski and McKenzie, issued Jan. 19, 1965, US. Pat. No. 3,220,959 of Orzechowski, issued Nov. 30, 1965 or US. Pat. No. 3,274,120 of Aftandilian, issued Sept. 20, 1966. The catalyst composition is also suitably prepared by the reaction of hydroxyl groups of titanium dioxide containing such groups with a silicon tetrahalide using the same surface reaction procedure disclosed in the above patents. In yet another technique, a catalyst composition comprising a fumed, pyrogenic titania-silica is prepared by the combustion of hydrogen and oxygen with a mixture of silicon tetrahalide and titanium halide in accordance with conventional methods of preparing finely-divided fumed metal oxides and silica. Other techniques for incorporating an oxide or hydroxide of titanium on an inorganic siliceous-solid such as dry-mixing, co-precipitation, impregnation and ion-exchange are also suitably employed.

The catalyst composition is optionally, and preferably, subject to a pretreatment or activation prior to utilization inthe process. The precise method of pretreatment will depend in part upon the form of chemical combination in which the components are provided, but in general the pretreatment comprises heating an initially prepared catalyst in an atmosphere of a nonreducing gas such as nitrogen, argon, carbon monoxide or oxygen-containing gas, e.g. air. One function served by this type of pretreatment operation is to convert the catalyst and catalyst promoter components into the form of hydroxides and oxides if these components are not initially provided in theseforms. For example, initial catalyst components such as titanium chloride, tetrakismethylpropylaminotitanium and potassium chloride are converted to the corresponding oxide by heating in a non-reducing atmosphere. The pretreatment temperature is not critical and temperatures from about 350C to about 800C are satisfactory. Typical pretreatment times are from 1 to 18 hours. Subsequent to pretreatment, the titanium catalyst is employed in any convenient physical form, for example, as powder, flakes, spheres or pellets.

The catalyst composition may suitably incorporate non-interfering substances, especially those that are inert to the reactants and products. The method of catalyst preparation is not critical to the functioning or effectiveness of the present invention.

The Silylation Treatment. In accordance with the invention, metal oxide-siliceous-solid epoxidation catalysts as herein described are improved by treatment with an organic silylating agent at elevated temperatures. As is often the case in the field of heterogeneous catalysis, the exact catalytic mechanism for epoxidation with these catalysts and the exact reason for their improvement with silylation are not known with certainty. It is recognized, however, that the silylation treatment imparts a hydrophobic character to the metal oxide/-silica catalysts. Also, it is known that the silylation agent reacts with active hydrogens, i.e.,

Bronsted acid sites on the catalyst surface, replacing them with organo-silicon groups.

Suitable silylating agents include the organosilanes, organosilylamines, and organosilazanes. One generally preferred class of silylating agents are the tetrasubstituted silanes having from 1 to 3 hydrocarbyl substituents, such as, for example, chlorotrimethylsilane, dichlorodimethylsilane, chlorobromodimethylsilane, ni-

trotrimethylsilane, chlorotriethylsilane, iododimethylbutylsilane and chlorodimethylphenylsilane. Very suitable silylating agents of this class comprise the tetrasubstituted silanes wherein at least one substituent is halogen selected from fluorine, chlorine, bromine and iodine and at least one substituent is hydrocarbyl of from 1 to 4 carbon atoms, that is, organohalosilanes. Preferred organohalosilane silylating agents are the tetrasubstituted silanes having'from l to 3 halo substituents selected from chlorine, bromine and iodine with the remainder of substituents being methyls. Particularly preferred organohalosilane silylating agents are dichlorodimethylsilane and chlorotrimethylsilane with chlorotrimethylsilane being most preferred.

Another generally preferred class of silylating agents are the organosilazanes, particularly the organodisilazanes. These materials are represented by formula (I) the six Rs independently are organic groups or hydrogens. Preferably the organosilazanes contain Rs which independently are hydrogens or alkyl groups of up to about 8 carbon atoms. Because of their method of production, these organosilazanes are symmetrical. Such silazanes include for example:

1,2-diethyldisilazane, l ,l ,2,Z-tetramethyldisilazane, 1,1 ,l ,2,2,2-hexamethyldisilazane, l,1,2,2-tetraethyldisilazane, and l,Z-diisopropyldisilazane. Of the organosilazanes, those in accord with formula I containing 4 or 6 lower alkyl groups, each of from 1 through 4 carbon atoms, and 0 or 2 hydrogens as their R groups are very preferred, with hexamethyldisilazane being the most preferred.

The two groups of preferred organic silylating agents each have advantages. The organohalosilane silylating agents are readily available and give excellent results under a variety of catalyst treatment conditions, although they pose a problem in that corrosive hydrogen halide is generated when they are used. The organosilazanes avoid the corrosion problem.

To effect the improving silylation, the metal oxidesilica chemical combination catalyst is contacted with a suitable silylating agent as herein defined, at elevated temperature. This may be accomplished in a variety of manners. For example, the catalyst particles may be mixed with a liquid silylating agent and then heated, or the catalyst particles may be heated and contacted with a stream of hot silylating agent vapor. The silylation may be carried out as a batch, semi-continuous or continuous process. Regardless of the method employed, best results are obtained with temperatures in the range of from about 100C to about 450C. With the organohalosilanes, temperatures of from about 300C to about 425C are preferred and temperatures of from about 375C to about 410 C are most preferred as they tend to give the most selective catalyst products. With the organosilazanes, temperatures of from 100C to 300C are preferred and temperatures of from 150C to 250C are most preferred.

The length of time required for the silylating agent to react with the catalyst surface depends in part on the temperature and agent employed. Lower temperatures require longer reaction times. Generally, times of from 0.1 to 48 hours are suitable. With the organohalosilanes, times of from 1 to 48 hours are typical. With 6 these agents, at a temperature of 325C, for example, times of from about 10 to 48 hours are preferred. At a temperature of 450C, 1 to 5 hours is preferred. With the organosilazanes 0.] to 5 hours is preferred.

The amount of silylating agent employed can vary widely. Amounts of silylating agent of from 1% by weight (basis the entire catalyst composition) to about by weight are suitable, with amounts of from 2 to 50% being preferred. The silylating agent can be applied to the catalyst either in one treatment or in a series of treatments. Generally a single treatment is preferred for reasons of operating economy.

It has been found that best results are often achieved by hydrating the metal/silica catalyst before silylation. Hydration is effected by contacting the catalyst prior to silylation with water and then heating it or by contacting the catalyst with steam at elevated temperatures, such as temperatures above C, preferably in the range of C to 450C for from about /2 to about 6 hours. When employing organosilazanes as silylating agents, best results are achieved when hydration is effected by steaming at a temperature of 300-450C for from about 1 to about 6 hours.

Epoxidation Catalysis. The solid silica/metal oxide catalysts when treated according to the invention are especially suitable for use as heterogeneous catalysts in liquid phase processes for epoxidation of olefinically unsaturated hydrocarbons by reaction with hydrocarbon hydroperoxides. Their use in such processes represents a major improvement therein, since markedly higher selectivities to olefin epoxide are achieved with treated catalysts than are possible with untreated catalysts at identical reaction conditions.

As olefinic reactant in this reaction may be employed any hydrocarbon having at least one aliphatic olefinically unsaturated carbon-carbon double bond, generally containing from 2 to 30 carbon atoms but preferably from 3 to 20 carbon atoms.

Preferred as olefinic reactant are the linear alpha alkenes of from 3 to 10 carbons such as propylene, butenel, pentene-l, ocetene-l and decene-l. Preferred hydrocarbon hydroperoxides are secondary and tertiary hydroperoxides of up to 15 carbon atoms, especially tertiary alkyl hydroperoxides such as tertiary butyl hydroperoxide; and aralkyl hydroperoxides wherein the hydroperoxy group is on a carbon atom attached directly to an aromatic ring, e.g., ahydroperoxy-substituted aralkyl compounds such as a-methylbenzyl hydroperoxide and cumene hydroperoxide.

In such an epoxidation process it is suitable to employ a molar ratio of olefinic reactant to hydroperoxide of at least 121 with ratios of from 2:1 to 20:1 being preferred.

The epoxidation reaction is conducted in the liquid phase in solvents or diluents which are liquid at reaction temperature and pressure and are substantially inert to the reactants and the products produced therefrom. Very suitable as solvents are hydrocarbons such as the hydrocarbon corresponding to the organic hydroperoxide, or alternatively excess olefin. The reaction is conducted at moderate temperatures and pressures. Suitable reaction temperatures vary from about 0C to about 200C, but preferably from 25C to 150C. The reaction is conducted at or above atmospheric pressure; The precise pressure is not critical so long as the reaction mixture is maintained substantially as liquid phase. Typical pressures vary from about 1 atmosphere to about 100 atmospheres. y

The olefin epoxide products are recovered from the resulting reaction product mixture by conventional means, e.g.. fractional distillation, extraction, fractional crystallization and chromatographic techniques.

The olefin oxide products of the epoxidation are materials of established utility and many are chemicals of commerce. For example, illustrative olefin oxides which are readily prepared by the process of the invention such as propylene oxide, 1,2-epoxybutane, 1,2- epoxy-Z-methyl-propane, 1,2-epoxydodecane and 1,2- epoxyhexadecane are formulated into useful polymers by polymerization or copolymerization as disclosed by U.S. Patents Nos. 2,815,343 2,871,219 and2,987,48 9.

The invention will be further described with reference to the following examples. There are for illustrative purposes only and are not to be construed as limitations on the invention.

EXAMPLE I A. A 300 g sample of commercial silica gel having a surface area of 340 m' /g and a pore volume of 1.15 cc/g (Davison, I.D. grade 59 silica) was contacted with a solution of 18 g of titanium tetachloride in 350 ml of methanol. The impregnated silica gel was dried at a temperature of 100C and then calcined at a temperature of 800C for 2 hours to produce a titania/silica product. 250 Grams of this calcined material was then rehydrated by contact with water for 10 hours to increase the number of silanol (Si O H) groups on the catalyst surface. This catalyst was then contacted with 50 mls of chlorotrimethylsilane as vapor for hours at 325-350C. The silylation was repeated twice. The catalyst preparation was repeated, without silylation. The resulting catalysts, (both'silylated and unsilylated) were compared. Analysis showed that each contained 1.5% by weight titanium. The silylated catalyst was hydrophobic while the unsilylated catalyst was hydrophilic.

B. The silylated and unsilylated titania-silica products of part A were compartively tested as olefin epoxidation catalysts. In each test a 1 gram sample of catalyst was contacted with 17 g of octene-l and 286g of a 12% by weight solution of ethylbenzenehydroperoxide in ethylbenzene in a 100 ml glass reactor. The reaction temperature was 100C and the reaction time was 1 hour. The results of these tests are given in Table I. The silylated catalyst gave markedly higher selectivity to the desired epoxide-forming reaction.

C. The epoxidation of propylene with ethylbenzene hydroperoxide was conducted in a 0.43 inch internal diameter 20 inch long fixed bed tubular reactor packed with 20 grams of the silylated titania-silica of Part A. A reaction mixture consisting of 6 moles of propylene per mole of ethylbenzene hydroperoxide in ethylbenzene was continuously fed to the reactor at a liquid hourly space velocity (LHSV) of 2 ccs per cc of catalyst per hour (hereinafter hr The reactor was maintained at the indicated temperature and a pressure of 450 psig. The reaction conditions and the analysis of the product mixture after the indicated cumulative operating time are provided in Table II. For purposes of comparison, the results of a similar test with an unsilylated 1.0% by weight titanium on silica catalyst additionally containing /z% by weight of calcium (prepared by the method of Example I) are provided in Table III.

Hours C Conversion. '71 Selectivity, 71

TABLE III Continuous Epoxidation with Unsilylated Catalyst Cumulative Temp.. Hydroperoxide Propylene Oxide Hours C Conversion. /r Selectivity. 71

EXAMPLE II A. Two silylated titania-silica catalysts were prepared. First, two 350 gram batches of calcined, unsilylated, 1.5% by weight titanium catalyst were prepared as described in part A of Example I. Then, these materials were each rehydrated with water and contacted with 50 grams of chlorotrimethylsilane for 15 hours. The first catalsyt (A) was silylated once at a temperature of 355-375C while the second catalyst (B) was silylated once at a temperature of 365-390C.

B. The silylated catalysts of part A were repeatedly tested as olefin epoxidation catalysts by the batch test described in part B of Example I, octene-l being epoxidized with ethylbenzenehydroperoxide. The results of these tests are given in Table IV.

C. Catalysts A and B were evaluated in the continuous propylene epoxidation reactor of Example I, Part C with the conditions and feeds of that Example. After 500 hours of operation, at C both catalysts A and B exhibited 9596% propylene oxide selectivity at 9596% hydroperoxide conversion.

TABLE IV Hydroperoxide Epoxidc Catalyst Conversion. 7t Selectivity, 71

A (silylated at 355-375C) 95-96 91-92 B (silylated at 365390C) 97-98 93-94 Unsilylatcd 94-96 79-81 *Prcparcd by the method of Example I. but with forced gas flow during calcination.

EXAMPLE III '9 then calcined at a temperature of 800C for 2 hours to produce a titania/silica product.

A 35 gram sample of this catalyst was then contacted with 20 mls of chlorotrimethyl silane as .vapor for hours at 325350C. This silylation was repeated twice. The resulting catalysts (both silylated and unsilylated) were compared. Analysis showed that each contained 1.0% by weight titanium. The silylated catalyst was hydrophobic, while the unsilylated catalyst was hydrophilic. I I

B. The epoxidation of propylene with ethylbenzenehydroperoxide was conducted in an 0.43 inch internal diameter inches long fixed bed tubular reactor packed with 20 grams of the silylated silica-titania catalyst of part A. This experiment was repeated with the catalystof part A, unsilylated. A reaction mixture consisting of 6 moles of propylene per mole of ethylbenzene hydroperoxide in ethylbenzene was continuously fed to the reactor, maintained at the indicated temperature and a pressure of 450 psig, at a rate giving a residence time of 24 minutes. The reaction conditions and analysis of the product mixture after the indicated reaction time are provided in Table V.

TABLE V Silylated Catalyst Cumulative Tcmp.-. Hydropcroxidc Propylene Oxide Hours C Conversion. Selectivity.

Unsilylated Catalyst 250 90 95-96 85-87 C. The silylated titania-silica product of part A was tested as octene-l epoxidation catalyst. In this test a 1 gram sample of catalyst was contacted with 36.5 g of octene-l and 4.5 g of 98% tertiarybutylhydroperoxide in a 100 ml glass reactor. The reaction temperature was l 0ll03C. After 1 hour, 73% of the hydroperoxide 'was converted (with 99% selectivity to octene oxide) and after 3 hours 90% was converted (also with 99% selectivity). l g,

EXAMPLE IV A. A 300 gram batch of calcined, unsilylated, 1.5%

by weight titanium catalyst'was prepared as described in part A of Example I. A 250 gram sample of this catalyst was then contacted with mls of dichlorodimethylsilane as vapor for 10 hours at 350C.

B. The silylatedand unsilylated products of part A were comparatively tested as olefin epoxidation cat alyst. In each test a 1 gram sample of catalyst was contacted with 17 g of octene-1 and 28.6 g of a 12% by weight solution of ethylbenzene hydroperoxide in ethylbenzene in a 100 ml glass reactor. The reaction temperature was 100C and the reaction time was 1 hour. The results of .these tests are given in Table .VI.

EXAMPLE v A calcined, unsilylated catalyst containing 1% by weight titanium and additionally /2%- by weight of calcium was prepared as described in part A of Example I.

A portion of this catalyst was then silylated at 360390C with trimethylchlorosilane.

Samples of both the silylated and unsilylated catalysts were tested by the batch epoxidation of Example I, Part B. The silylated material gave 91% selectivityto propylene oxide at 78% come rsion while the untreated material gave 86% selectivity at 83% conversion.

EXAMPLE VI A 1.5% by weight titanium-on-silica catalyst was prepared bytreating an acidic silica hydrogelwith a titanium salt solution, adding base to the mixture, drying and then calcining. 1

A sample of this catalyst was then treated with trimethylchlorosilane in benzene at 60'70C for 2 hours and dried-at 150C for 2 hours. I

A single sample of silylated material was then repeatedly used as a catalyst for the batch epoxidation of octene-l with ethylbenzene hydroperoxide using the apparatus, feeds and conditions of Example 1, part B. The results of the repeated 1 hour tests are given in Table VII.

TABLE v11 A. A l480 grambatch of the commercial silica gel (Davis on I.D. grade silica 14-30 mesh) was contacted with a solution of 130 grams of tetraisopropyltitanate and 97 grams of acetylace tone in 1.25 liters of isopropyl alcohol. The impregnated silica gel was charged to i an electrically heated calcination'tube and dried to a bed temperature of 500C under a nitrogen blanket. Air was then admitted and the temperature was raised to 800C and there held for 4 hours to burn off residual carbon and thoroughly chemically combine the silica and titania. l 183 Grams of this material was then rehydrated by contact with steam at 400C for 3 hours. This rehydrated material was cooled to 200C then contacted with hexamethyldisilazane vapor at 200C for 1 hour to give a silylated catalyst in accord with this invention. Grams of hexamethyldisilazane were taken up by the catalyst.

B. The catalyst of part A, with and without silylation was tested as a catalyst for the epoxidation of olefins with hydroperoxide using the apparatus, feedstocks and general procedures of Example 1 part B. The results of these tests are given in Table Vlll.

TA BLE VIII Hyd roperoxide Epoxidc Catalyst Conversion, 7! Selectivity. 7:

Unsilylatcd 72 TABLE VIII-continued Hydropcroxidc Epoxide Catalyst Conversion, 7 Selectivity. "/1

Silylatcd 95 93.

I claim as my invention:

1. A process for the epoxidation of an olefinically unsaturated compound which comprises reacting the olefinically unsaturated compound in the liquid phase with an organic hydroperoxide at a temperature of from about C to about 200C in the presence of a catalyst prepared by reacting an olefin epoxidation catalyst comprising an inorganic siliceous solid in chemical combination with an oxide or hydroxide of titanium with an organic silylating agent at an elevated silylation temperature in the range from about 100 to about 450C for from about 0.1 to 48 hours.

2. A process for the epoxidation of an olefinically unsaturated compound which comprises reacting the olefinically unsaturated compound in the liquid phase with an organic hydroperoxide at a temperature of from about 25C to about 200C in the presence of a catalyst prepared by reacting an olefin epoxidation catalyst comprising an inorganic siliceous solid in chemical combination with an oxide or hydroxide of titanium for a time period of from 0.1 to 48 hours, at a temperature from about 100C to about 450C, with an organic silylating agent selected from the group consisting of (a) trihalomonohydrocarbylsilanes, dihalo-dihydrocarbylsilanes and mono-halotrihydrocarbylsilanes wherein the halo substituents are selected from the group consisting of chloro. bromo. and iodo, and (b) organodisilazanes having the structural formula wherein 4 or 6 of the R's independently are lower alkyls of from 1 through 4 carbon atoms and the other R's independently are hydrogens.

3. The process of claim 2 wherein the olefinically unsaturated compound is an alkene of from 3 to 20 carbon atoms and the organichydroperoxide is selected from the group consisting of tertiary alkyl hydroperoxides and aralkyl hydroperoxides.

4. The process of claim 3 wherein the alkene is a linear alkene of from 3 to 10 carbon atoms, the hydrocarbyl substituents in the halosilanes each have from one to four carbon atoms and all the Rs in said organodisilazanes are lower alkyl groups of one to four carbon atoms.

5. The process of claim 4 wherein the alkene is propylene.

6. The process of claim 2 wherein the silylating agent is chosen from the group consisting of trihalomonohydrocarbylsilane, dihalodihydrocarbylsilane, and monohalotrihydrocarbylsilane; the halo substituents are selected from the group consisting of chloro, bromo and iodo; the hydrocarbyl substituents each have from 1 to 4 carbon atoms; the silylation reaction time is from about 1 to 48 hours; and the silylation reaction temperature is from about 300C to 450C.

7. The process of claim 6 wherein the organic silylating agent is chlorotrimethylsilane.

12 8. The process of claim 6 wherein said unsaturated compound is propylene.

9. The process of claim 2 wherein the silylating agent is an organodisilazane H and the silylation reaction time is from 0.1 to 5 hours.

10. The process of claim 9 wherein every R is methyl.

11. The process of clam 9 wherein said unsaturated compound is propylene.

12. The process for the epoxidation of a linear alpha alkene of from 3-20 carbon atoms which comprises reacting the linear alpha alkene with an organic hydroperoxide in the presence of a catalyst prepared by reacting an olefin epoxidation catalyst comprising an inorganic siliceous solid containing a major portion of silica in chemical combination with from 0.2 to 10% by weight of total catalyst of. titanium oxide or hydroxide for from 0.1 to 48 hours at a temperature of from C to about 450C with an organic silylating agent selected from the group consisting of (a) trihalomonohydrocarbylsilanes, dihalo-dihydrocarbylsilanes and monohalotrihydrocarbylsilanes wherein the halo substituents are selected from the group consisting of chloro, bromo, and iodo and the hydrocarbyl substituents each have from 1 to 4 carbon atoms and (b) organodisilazanes having the structural formula wherein 4 or 6 of the Rs independently are lower alkyls of from 1 through 4 carbon atoms and the other Rs independently are hydrogens.

13. The process of claim 12 wherein said alkene is propylene and said silylating agent is chlorotrimethylsilane.

14. The process of claim 12 wherein said alkene is propylene and said silylating agent is an organodisilazane of the formula wherein R is alkyl of l to 4 carbon atoms.

15. The process of claim 14 wherein every R is methyl.

16. A process for the epoxidation of an olefinically unsaturated compound which comprises reacting the olefinically unsaturated compound in the liquid phase with an organic hydroperoxide at a temperature of from about 25C to about 200C in the presence of a catalyst prepared by reacting an olefin epoxidation catalyst comprising an inorganic siliceous solid in chemical combination with an oxide or hydroxide of titanium for a time period of from 0.1 to 48 hours, at a temperature from about 100C to about 450C, with an organic silylating agent selected from the group consisting of (a) tetrasubstituted silanes having from 1 to 3 hydrocarbyl substituents wherein the halo substituents are selected from the group consisting of chloro, bromo, and iodo and (b) organodisilazanes having the structural formula wherein the 6 Rs independently are lower alkyls of from 1 through 8 carbon atoms or hydrogens.

17. The process for the epoxidation of propylene which comprises reacting propylene with ethylbenzene hydroperoxide, cumene hydroperoxide or tertiary butyl hydroperoxide at a temperature of from about C to about 200C in the presence of a catalyst prepared by reacting an olefin epoxidation catalyst comprising an inorganic siliceous solid containing at least 99% silica in chemical combination with from 0.2 to 10% by weight of total catalyst of titanium oxide or hydroxide 14 for a time period of from 1 to 48 hours at a temperature of from about 300C to about 425C with chlorotrimethylsilane as silylating agent.

18. The process for the epoxidation of propylene which comprises reacting propylene with ethylbenzene hydroperoxide, cumene hydroperoxide or tertiary butyl hydroperoxide at a temperature of from about 25C to about 200C in the presence of a catalyst prepared by reacting an olefin epoxidation catalyst comprising an inorganic siliceous solid containing at least 99% silica in chemical combination with from 0.2 to 10% by weight of total catalyst of titanium oxide or hydroxide for a time period of from about 0. l to 5 hours at a temperature of from about C to 300C with hexamethyldisilazane as silylating agent. 

1. A PROCESS FOR THE EPOXIDATION OF AN OLEFINICALLY UNSATURATED COMPOUND WHICH COMPRISES REACTING THE OLEFINICALLY UNSATURATED COMPOUND IN THE LIQUID PHASE WITH AN ORGANIC HYDROPEROXIDE AT A TEMPERATURE OF FROM ABOUT 25*C TO ABOUT 200*C IN THE PRESENCE OF A CATALYST PREPARED BY REACTING AN OLEFIN EPOXIDATION CATALYST COMPRISING AN INORGANIC SILICEOUS SOLID IN CHEMICAL COMBINATION WITH AN OXIDE OR HYDROXIDE OF TITANIUM WITH AN ORGANIC SILYLATING AGENT AT AN ELEVATED SILYLATION TEMPERATURE IN THE RANGE FROM ABOUT 100* TO ABOUT 450*C FOR FROM ABOUT 0.1 TO 48 HOURS.
 2. A process for the epoxidation of an olefinically unsaturated compound which comprises reacting the olefinically unsaturated compound in the liquid phase with an organic hydroperoxide at a temperature of from about 25*C to about 200*C in the presence of a catalyst prepared by reacting an olefin epoxidation catalyst comprising an inorganic siliceous solid in chemical combination with an oxide or hydroxide of titanium for a time period of from 0.1 to 48 hours, at a temperature from about 100*C to about 450*C, with an organic silylating agent selected from the group consisting of (a) trihalomonohydrocarbylsilanes, dihalo-dihydrocarbylsilanes and mono-halotrihydrocarbylsilanes wherein the halo substituents are selected from the group consisting of chloro, bromo, and iodo, and (b) organodisilazanes having the structural formula
 3. The process of claim 2 wherein the olefinically unsaturated compound is an alkene of from 3 to 20 carbon atoms and the organic hydroperoxide is selected from the group consisting of tertiary alkyl hydroperoxides and aralkyl hydroperoxides.
 4. The process of claim 3 wherein the alkene is a linear alkene of from 3 to 10 carbon atoms, the hydrocarbyl substituents in the halosilanes each have from one to four carbon atoms and all the R''s in said organodisilazanes are lower alkyl groups of one to four carbon atoms.
 5. The process of claim 4 wherein the alkene is propylene.
 6. The process of claim 2 wherein the silylating agent is chosen from the group consisting of trihalomonohydrocarbylsilane, dihalodihydrocarbylsilane, and monohalotrihydrocarbylsilane; the halo substituents are selected from the group consisting of chloro, bromo and iodo; the hydrocarbyl substituents each have from 1 to 4 carbon atoms; the silylation reaction time is from about 1 to 48 hours; and the silylation reaction temperature is from about 300*C to 450*C.
 7. The process of claim 6 wherein the organic silylating agent is chlorotrimethylsilane.
 8. The process of claim 6 wherein said unsaturated compound is propylene.
 9. The process of claim 2 wherein the silylating agent is an organodisilazane
 10. The process of claim 9 wherein every R is methyl.
 11. The process of clam 9 wherein said unsaturated compound is propylene.
 12. The process for the epoxidation of a linear alpha alkene of from 3-20 carbon atoms which comprises reacting the linear alpha alkene with an organic hydroperoxide in the presence of a catalyst prepared by reacting an olefin epoxidation catalyst comprising an inorganic siliceous solid containing a major portion of silica in chemical combination with from 0.2 to 10% by weight of total catalyst of titanium oxide or hydroxide for from 0.1 to 48 hours at a temperature of from 100*C to about 450*C with an organic silylating agent selected from the group consisting of (a) trihalomonohydrocarbylsilanes, dihalo-dihydrocarbylsilanes and monohalotrihydrocarbylsilanes wherein the halo substituents are selected from the group consisting of chloro, bromo, and iodo and the hydrocarbyl substituents each have from 1 to 4 carbon atoms and (b) organodisilazanes having the structural formula
 13. The process of claim 12 wherein said alkene is propylene and said silylating agent is chlorotrimethylsilane.
 14. The process of claim 12 wherein said alkene is propylene and said silylating agent is an organodisilazane of the formula
 15. The process of claim 14 wherein every R is methyl.
 16. A process for the epoxidation of an olefinically unsaturated compound which comprises reacting the olefinically unsaturated compound in the liquid phase with an organic hydroperoxide at a temperature of from about 25*C to about 200*C in the presence of a catalyst prepared by reacting an olefin epoxidation catalyst comprising an inorganic siliceous solid in chemical combination with an oxide or hydroxide of titanium for a time period of from 0.1 to 48 hours, at a temperature from about 100*C to about 450*C, with an organic silylating agent selected from the group consisting of (a) tetrasubstituted silanes having from 1 to 3 hydrocarbyl substituents wherein the halo substituents are selected from the group consisting of chloro, bromo, and iodo and (b) organodisilazanes having the structural formula
 17. The process for the epoxidation of propylene which comprises reacting propylene with ethylbenzene hydroperoxide, cumene hydroperoxide or tertiary butyl hydroperoxide at a temperature of from about 25*C to about 200*C in the presence of a catalyst prepared by reacting an olefin epoxidation catalyst comprising an inorganic siliceous solid containing at least 99% silica in chemical combination with from 0.2 to 10% by weight of total catalyst of titanium oxide or hydroxide for a time period of from 1 to 48 hours at a temperature of from about 300*C to about 425*C with chlorotrimethylsilane as silylating agent.
 18. The process for the epoxidation of propylene which comprises reacting propylene with ethylbenzene hydroperoxide, cumene hydroperoxide or tertiary butyl hydroperoxide at a temperature of from about 25*C to about 200*C in the presence of a catalyst prepared by reacting an olefin epoxidation catalyst comprising an inorganic siliceous solid containing at least 99% silica in chemical combination with from 0.2 to 10% by weight of total catalyst of titanium oxide or hydroxide for a time period of from about 0.1 to 5 hours at a temperature of from about 150*C to 300*C with hexamethyldisilazane as silylating agent. 